| SUPERFLEX™ Fabric, 630 g/m2 (18.5 oz/yd2) |
|
| Description : |
|
A 260ºC (500ºF) maximum service temperature, patented expanded polytetrafluoroethylene fiber/fiberglass composite fabric filter bag for use in pulse jet style dust collectors.
|
| Features And Benifits : |
- Patented Lyallpur Enterprises high-durability membrane technology provides an excellent combination of filtration efficiency and dust cake release.
- Patented expanded polytetrafluoroethylene-coated fiberglass fiber composite provides good all-around chemical and temperature resistance with superior flex resistance.
- Patented fabric design and construction provides excellent dimensional stability, superior flexibility, and resistance to mechanical damage over the life of the filter.
|
| Applications : |
- Chemicals Processing : Dryers and micronizers in TiO2 and pigment industries.
- Minerals Processing : Cement kiln/mill, alkali bypass, lime kiln, and lightweight aggregate dust collectors.
- Metals Processing : Iron and steel production foundries and ferro-alloy production.
- Power Generation and Incineration : Incinerators and boilers.
|
| Technical Specification : |
| Fiber Content |
Fluoropolymer-fiberglass Composite |
| Fabric Construction |
Double-Filling Face |
| Continuous Operating Temperature |
260ºC (500ºF) |
| Maximum Surge Temperature |
274ºC (525ºF) |
| Acid Resistance |
Very Good |
| Alkali Resistance |
Fair |
| Breaking Strength |
| - Machine Direction |
2500 N/2.54 cm (560 lb/1 in) ravel |
| - Cross-Machine Direction |
2200 N/2.54 cm (500 lb/1 in) ravel |
| Mullen Burst |
5500 kPa (800 psi) |
| Thickness |
0.86 mm (0.034 in) |
| MIT Flex |
Over 1,000,000 cycles |
|
|